Charged hollow fiber membrane having hexagonal voids

ABSTRACT

Disclosed is a charged hollow fiber membrane having hexagonal voids for use in high throughput applications. The membrane includes: (i) an inner surface; (ii) an outer surface; (iii) a porous bulk disposed therebetween, wherein the porous bulk comprises at least a first region including: a) a first set of pores having a controlled pore size and having outer rims; b) a second set of pores connecting the outer rims of the first set of pores, wherein the pore size of the first set of pores is greater than the pore size of the second set of pores; and c) a polymer matrix supporting the first set of pores; and (iv) at least one charged zone disposed on the inner surface, on the outer surface, and/or in the porous bulk hollow fiber membrane. Also disclosed is a method for preparing such hollow fiber membranes, which involves coating a filament with a coating composition that includes a membrane-forming polymer, a charged polymer, and dissolvable nanoparticles, followed by phase invention, dissolving of the nanoparticles, and removal of the filament.

BACKGROUND OF THE INVENTION

Charged hollow fiber membranes are used to filter a variety of fluids. However, there is a need for charged hollow fiber membranes that provide high throughput performance.

The present invention provides for ameliorating at least some of the disadvantages of the prior art. These and other advantages of the present invention will be apparent from the description as set forth below.

BRIEF SUMMARY OF THE INVENTION

An embodiment of the invention provides a charged hollow fiber membrane comprising: (i) an inner surface; (ii) an outer surface; (iii) a porous bulk disposed between the inner surface and the outer surface, wherein the porous bulk comprises at least a first region including: a) a first set of pores having a controlled pore size and having outer rims; b) a second set of pores connecting the outer rims of the first set of pores, wherein the pore size of the first set of pores is greater than the pore size of the second set of pores; and c) a polymer matrix supporting the first set of pores; and (iv) at least one charged zone disposed on the inner surface, on the outer surface, and/or in the porous bulk hollow fiber membrane.

In an embodiment, the invention provides a hollow fiber membrane comprising (i) an inner surface; (ii) an outer surface; and (iii) a porous bulk disposed between the inner surface and the outer surface, wherein the porous bulk comprises a first region and a second region, wherein the first region includes: a) a first set of pores having a controlled pore size and having outer rims; b) a second set of pores connecting the outer rims of the first set of pores, wherein the pore size of the first set of pores is greater than the pore size of the second set of pores, and the second region includes a) a third set of pores having a controlled pore size having outer rims; b) a fourth set of pores connecting the outer rims of the third set of pores, wherein the pore size of the third set of pores is greater than the pore size of the fourth set of pores and c) a polymer matrix supporting the third set of pores; and at least one charge zone disposed on the inner surface, on the outer surface, in the first region, and/or the second region.

In accordance with other embodiments of the invention, filters and filter devices comprising the charged hollow fiber membranes, as well of methods of making and using the charged hollow fiber membranes, are provided.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWING(S)

FIG. 1 is an illustration of the pores and voids present in at least some parts of the hollow fiber membrane according to an embodiment of the invention, showing a first set of pores having connecting outer rims (one pore highlighted in dashed lines), and a second set of pores (one pore highlighted in solid line) located in the connecting outer rims of the first set of pores.

FIG. 2 illustrates hexagonal packing of the first set of pores (formed by dissolving of particles) in a membrane according to an embodiment of the invention, wherein the hexagonal packing is 74 volume percent. FIG. 2 also illustrates the matrix (“polymer formed interstitials”) supporting the first set of pores, and the second set of pores connecting the outer rims of the first set of pores.

FIG. 3A depicts an SEM of a charged PES hollow fiber membrane in accordance with an embodiment of the invention illustrated in Example 2. FIG. 3B is a higher magnification SEM of the hollow fiber membrane depicted in FIG. 3A showing the two charged zones.

FIG. 4A depicts an SEM of a charged PES hollow fiber membrane in accordance with an embodiment of the invention illustrated in Example 3. FIG. 4B is a higher magnification SEM of the hollow fiber membrane showing the two charged zones.

DETAILED DESCRIPTION OF THE INVENTION

An embodiment of the invention provides a charged hollow fiber membrane comprising: (i) an inner surface; (ii) an outer surface; (iii) a porous bulk disposed between the inner surface and the outer surface, wherein the porous bulk comprises at least a first region including: a) a first set of pores having a controlled pore size and having outer rims; b) a second set of pores connecting the outer rims of the first set of pores, wherein the pore size of the first set of pores is greater than the pore size of the second set of pores; and c) a polymer matrix supporting the first set of pores; and (iv) at least one charged zone disposed on the inner surface, on the outer surface, and/or in the porous bulk hollow fiber membrane.

In accordance with an embodiment, the pore size of the first set of pores is in the range of from about 50 nm to about 1000 nm, for example, from about 160 nm to about 630 nm. Thus, for example, the pore size of the first set of pores is about 160 nm, about 180 nm, about 200 nm, about 220 nm, about 240 nm, about 260 nm, about 280 nm, about 300 nm, about 320 nm, about 340 nm, about 360 nm, about 380 nm, about 400 nm, about 420 nm, about 440 nm, about 460 nm, about 480 nm, about 500 nm, about 520 nm, about 540 nm, about 560 nm, about 580 nm, about 600 nm, or about 620 nm.

In an embodiment, the pore size of the second set of pores is in a ratio in the range of about 0.2 to about 0.4 times the pore size of the corresponding first set of pores.

In an embodiment, the invention provides a hollow fiber membrane comprising (i) an inner surface; (ii) an outer surface; and (iii) a porous bulk disposed between the inner surface and the outer surface, wherein the porous bulk comprises a first region and a second region, wherein the first region includes: a) a first set of pores having a controlled pore size and having outer rims; b) a second set of pores connecting the outer rims of the first set of pores, wherein the pore size of the first set of pores is greater than the pore size of the second set of pores, and the second region includes a) a third set of pores having a controlled pore size and having outer rims; b) a fourth set of pores connecting the outer rims of the third set of pores, wherein the pore size of the third set of pores is greater than the pore size of the fourth set of pores and c) a polymer matrix supporting the third set of pores; and at least one charge zone disposed on the inner surface, on the outer surface, in the first region, and/or the second region.

In an embodiment, the pore size of the fourth set of pores is in a ratio in the range of about 0.2 to about 0.4 times the pore size of the third set of pores.

In an embodiment, the pore size of the third set of pores is at least 10%, for example, 20%, 30%, 40%, 50%, 60%, 70%, or 80%, different from the pore size of the first set of pores. The pore size of the third set of pores can be larger or smaller than the pore size of the first set of pores.

The present invention further provides a method of making a charged hollow fiber membrane, the method comprising: (a) forming at least one coating composition comprising a solvent, dissolvable nanoparticles, a membrane-forming polymer, and a charged polymer; (b) coating the at least one coating composition onto a filament; (c) carrying out phase inversion of the at least one coating composition, or the coating compositions, coated onto the filament; (d) dissolving the dissolvable nanoparticles and removing the filament from the coated filament to obtain a charged hollow fiber membrane; and optionally (e) washing the charged hollow fiber membrane obtained in (d).

In an embodiment, the charged hollow fiber membrane is prepared by introducing dissolvable nanoparticles into solutions containing one or more membrane forming polymers and a charged polymer (typically, the membrane forming polymers and charged polymers are dissolved in a solvent or mixture of solvents), casting the nanoparticle-containing polymer solution or composition (preferably, casting the nanoparticle-containing polymer composition on a substrate such as a filament or fiber wherein the substrate has been pretreated with a preconditioning or releasing agent; more preferably, wherein the agent has been dried on the substrate before casting the solution thereon), carrying out phase inversion of the nanoparticle-containing composition to provide a membrane, subsequently dissolving the nanoparticles, and washing the resultant membrane. Preferably, the dissolvable nanoparticles comprise silica nanoparticles, especially ones having high surface area or low density.

Advantageously, charged hollow fiber membranes according to the invention can be produced using preformed membrane-forming polymers such as polyethersulfone (PES), polyvinylidene fluoride (PVDF), and polyacrylonitrile (PAN), that are commonly used in commercial membranes, in combination with one or more charge providing polymers.

The charged polymers are polymers that provide a positive or negative charge. Positively charged polymers can be any polymer that carries a positive charge or can become positively charged when exposed to fluids. Thus, for example, polymers bearing amino, imino, ammonium, or phosphonium groups in the backbone, pendant groups, and/or on the chain ends are suitable. Examples of polymers having positive charge include polyethylenimine, polydiallyldimethylammonium chloride, polyvinylamine, amine terminated polyethylene oxide or polyethylene glycol, poly(2-vinylpyridine), poly(4-vinylpyridine), and poly(l-vinylpyrrolidone-co-2-dimethylaminoethylmethacrylate).

Negatively charged polymers can be any polymer that carries a negative charge or can become negatively charged when exposed to fluids. Thus, for example, polymers bearing carboxyl, sulfonic, or phosphonic groups in the backbone, pendant groups, and/or chain ends are suitable. Examples of polymers having negative charge include maleic acid:methyl vinyl ether copolymer, polystyrene sulfonic acid, sulfonated polysufone, sulfonated polyether sulfone, polyacrylic acid, polymethacrylic acid, and polyvinylphenol.

The nanoparticles employed in the preparation of the charged hollow fiber membrane is preferably one that can be dissolved without using hydrofluoric acid, for example, the nanoparticles can be dissolved using safer, more environmentally benign solvents such as an alkaline solution.

In other embodiments, filters and filter devices are provided, the filter and filter devices comprising at least one hollow fiber membrane.

A method of filtering fluid is also provided in accordance with another embodiment of the invention, the method comprising passing the fluid through at least one membrane, or a filter comprising at least one membrane, as described above.

In accordance with an embodiment of the invention, a method of preparing a charged hollow fiber membrane comprises (a) forming a composition comprising silica nanoparticles, membrane-forming polymer and a charged polymer; (b) coating the composition onto a filament substrate; (c) carrying out phase inversion of the coated nanoparticle-containing coating composition to provide a membrane; (d) dissolving the nanoparticles and obtaining a nanoparticle-depleted membrane; and (e) removing the filament substrate to obtain the charged hollow fiber membrane. Preferably (b) comprises casting the coating composition onto a filament substrate pretreated with a preconditioning agent or a release agent. In some embodiments of the method, the preconditioning agent or the release agent is dried on the substrate before casting the coating composition on the pretreated substrate. In some embodiments, (c) comprises immersing the coated filament in a liquid to obtain the membrane. Alternatively, or in addition, the coated filament can be phase inverted by exposing it to a temperature in the range of from about 40° C. to about 80° C. for a period in the range of from about 1 minute to about 2 hours.

As will be described in more detail below, dissolving the particles creates a first set of pores in the membranes, the first set of pores having outer rims, and located within the outer rims is a second set of pores. As illustrated in FIG. 1, the dashed line highlights an outer rim of a pore in the first set, and the solid line highlights a pore in the second set. The second set of pores allows communication (e.g., fluid flow) from the void within one outer rim into the void of another outer rim.

A variety of dissolvable nanoparticles are suitable for use in preparing membranes according to embodiments of the invention. The dissolvable particles are not pure silica. Preferably, the nanoparticles comprise silica, typically ranging in diameter from about 50 nm to about 1000 nm. In accordance with an embodiment, the present invention provides silica nanoparticles having a diameter of about 50 nm to about 1000 nm and a particle density of about 1.96 g/cm³ or less.

In an embodiment, the silica nanoparticles of the invention having a particle density of about 1.93 to about 1.96 g/cm³.

The silica nanoparticles can have a particle size, e.g., diameter, of less than 1000 nm, in particular a particle size of from about 160 nm to about 630 nm. Thus, for example, the nanoparticles have a particle size of about 160 nm, about 180 nm, about 200 nm, about 220 nm, about 240 nm, about 260 nm, about 280 nm, about 300 nm, about 320 nm, about 340 nm, about 360 nm, about 380 nm, about 400 nm, about 420 nm, about 440 nm, about 460 nm, about 480 nm, about 500 nm, about 520 nm, about 540 nm, about 560 nm, about 580 nm, about 600 nm, or about 620 nm.

The silica nanoparticles can be prepared by a method comprising: (a) reacting an orthosilicate and an alcohol or a mixture of alcohols in an aqueous medium in the presence of a salt of a metal of Group Ia or Group IIa, or in the presence of a metalloid compound, optionally in combination with ammonium hydroxide, (b) isolating the resulting nanoparticles, and (c) treating the nanoparticles from (b) with an acid.

In an embodiment, the nanoparticles can be included in the coating composition prior to the acid treatment (c).

In an embodiment, the orthosilicate used in the preparation of the nanoparticles is a tetraalkylorthosilicate. Examples of tetraalkylorthosilicates tetramethylorthosilicate, tetraethylorthosilicate, tetrapropylorthosilicate, tetrabutylorthosilicate, and tetrapentylorthosilicate.

Any suitable alcohol or mixture of alcohols can be used in the preparation of the nanoparticles, for example, the alcohol or mixture of alcohols is selected from methanol, ethanol, propanol, butanol, and mixtures thereof

The salt of the metal used in the preparation of the nanoparticles can be selected from salts of lithium, sodium, potassium, cesium, magnesium, and calcium. In an embodiment, the salt of the metal is selected from lithium acetate, sodium acetate, sodium metasilicate, sodium formate, potassium acetate, cesium acetate, magnesium acetate, and calcium acetate. In another embodiment, the metalloid compound is a compound of boron, for example, boric acid or a boric acid ester such as alkyl borate. The alkyl borate can be a trialkyl borate such as trimethyl borate or triethyl borate.

In (c), any suitable acid can be employed, preferably a mineral acid or an organic acid. Examples of mineral acids include hydrochloric acid, sulfuric acid, and nitric acid, preferably hydrochloric acid or sulfuric acid. Examples of organic acids include acetic acid, formic acid, trifluoroacetic acid, trichloroacetic acid, and p-toluenesulfonic acid, preferably formic acid. The nanoparticles isolated in (b) can be treated with a 1N to 2N acid, e.g., 1N HC1, for a period of about 0.5 hr to about 3 hr, preferably about 1 hr to 2 hr. For example, the nanoparticles can be sonicated in an acid bath for the above period. Following the acid treatment, the nanoparticles are isolated from the acid and washed with deionized water and dried under vacuum to obtain the silica nanoparticles.

Illustratively, silica nanoparticles was prepared as follows. In a 6 L jacketed flask kept at 25° C., 4.8 g lithium acetate dihydrate (LiOAc. 2H₂O), 2480 mL deionized water (DI-H₂O), 2.9 L anhydrous ethanol (EtOH), and 120 mL 28% w/w NH₃ in water were stirred for 30 min at 200 rpm using an overhead mixer with PTFE impellers. A solution of 300 mL EtOH with 200 mL tetraethylorthosilicate (TEOS), which was prepared under dry conditions (<10% relative humidity), was rapidly poured into the 6 L flask, and mixing was increased to 400 rpm and a dry air purge (<1% relative humidity) was utilized for 5 min. Mixing was reduced to 200 rpm, the dry air purge was removed, the flask was sealed, and the reaction continued for a total of 1 h. The particles were purified by centrifugation and re-suspension in EtOH three times. The particles prepared as above can be used as such in the preparation of the coating composition for preparing the hollow fiber membrane, or alternatively, they can be treated with HCl before preparing the coating composition.

Thus, the particles were sonicated with 1N HCl, washed with DI water, and dried under vacuum at 40° C.

Typical coating compositions (dispersions) comprising the dissolvable nanoparticles, preferably purified dissolvable nanoparticles, comprise the nanoparticles dispersed at concentrations in the range of from about 30 wt % to about 65 wt % dimethyl formamide (DMF), within the range of from about 0.001% to about 0.1% triethanolamine (TEA).

A membrane-forming polymer solution is prepared by dissolving the polymer in a solvent or a mixture of solvents. A variety of polymers is suitable for use as membrane-forming polymers in the invention, and is known in the art. Suitable polymers can include, polymers such as, for example, polyaromatics; sulfones (e.g., polysulfones, including aromatic polysulfones such as, for example, polyethersulfone (PES), polyether ether sulfone, bisphenol A polysulfone, polyarylsulfone, and polyphenylsulfone), polyamides, polyimides, polyvinylidene halides (including polyvinylidene fluoride (PVDF)), polyolefins, such as polypropylene and polymethylpentene, polyesters, polystyrenes, polycarbonates, polyacrylonitriles ((PANs) including polyalkylacrylonitriles), cellulosic polymers (such as cellulose acetates and cellulose nitrates), fluoropolymers, and polyetherether ketone (PEEK). Polymer solutions can include a mixture of polymers, e.g., a hydrophobic polymer (e.g., a sulfone polymer) and a hydrophilic polymer (e.g., polyvinylpyrrolidone (PVP)).

In addition to one or more polymers, typical polymer solutions comprise at least one solvent, and may further comprise at least one non-solvent. Suitable solvents include, for example, dimethyl formamide (DMF); N,N-dimethylacetamide (DMAC); N-methyl pyrrolidone (NMP); dimethyl sulfoxide (DMSO), methyl sulfoxide, tetramethylurea; dioxane; diethyl succinate; chloroform; and tetrachloroethane; and mixtures thereof. Suitable nonsolvents include, for example, water; various polyethylene glycols (PEGs; e.g., PEG-200, PEG-300, PEG-400, PEG-1000); various polypropylene glycols; various alcohols, e.g., methanol, ethanol, isopropyl alcohol (IPA), amyl alcohols, hexanols, heptanols, and octanols; alkanes, such as hexane, propane, nitropropane, heptanes, and octane; and ketone, ethers and esters such as acetone, butyl ether, ethyl acetate, and amyl acetate; acids, such as acetic acid, citric acid, and lactic acid; and various salts, such as calcium chloride, magnesium chloride, and lithium chloride; and mixtures thereof.

If desired, a solution comprising a polymer can further comprise, for example, one or more polymerization initiators (e.g., any one or more of peroxides, ammonium persulfate, aliphatic azo compounds (e.g., 2,2′-azobis(2-amidinopropane) dihydrochloride (V50)), and combinations thereof), and/or minor ingredients such as surfactants and/or release agents.

Typical stock solutions including a polymer (before combining with a solution comprising the dissolvable nanoparticles) comprise in the range of from about 10 wt % to about 35 wt % resin (e.g., PES, PVDF, or PAN), in the range of from about 0 to about 10 wt % PVP, in the range of from about 0 to about 10 wt % PEG, in the range of from about 0 to about 90 wt % NMP, in the range of from about 0 to about 90 wt % DMF, and in the range of from about 0 to about 90 wt % DMAC. When a charged polymer is included in the stock solutions, the charged polymer can be present in an amount of up to about 5 wt % relative to total resin only (e.g., 5 PHR).

Suitable components of solutions are known in the art. Illustrative solutions comprising polymers, and illustrative solvents and nonsolvents include those disclosed in, for example, U.S. Pat. Nos. 4,340,579; 4,629,563; 4,900,449; 4,964,990, 5,444,097; 5,846,422; 5,906,742; 5,928,774; 6,045,899; 6,146,747; and 7,208,200.

While a variety of polymeric membranes can be produced in accordance with the invention, in preferred embodiments, the membranes are sulfone membranes (more preferably, polyethersulfone membranes and/or polyarylsulfone membranes), acrylic membranes (e.g., (PANs, including polyalkylacrylonitriles), or semi-crystalline membranes (for example, PVDF membranes and/or polyamide membranes).

The coating composition can be coated on a filament by any suitable technique, for example, by dip coating or spray coating.

A variety of filaments are suitable for coating the coating composition according to embodiments of the invention. Suitable filaments include, for example, glass, a polyester such as polyethylene terephthalate (PET); polypropylene; polyethylene (including polyethylene naphthalate (PEN); polyethylene terephthalate glycol (PETG)); polyimide; polyphenylene oxide; nylons, particularly polycaprolactam; and acrylics. Preferably, the filament is a monofilament. The filament can be of any suitable thickness depending on the desired inner diameter of the hollow fiber membrane. The filaments are typically circular in cross-section and about 0.1 mil to about 10 mils thick, for example, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10 mils thick.

In some embodiments, the filament has been preconditioned with a preconditioning agent, preferably, wherein the agent is dried before the particle-containing polymer composition is cast on the pretreated filament. Without being bound to any particular theory, it is believed that, with respect to some filaments, the use of a preconditioning agent improves efficiency in separating the charged hollow fiber membrane from the filament.

Preferably, the preconditioning agent does not dissolve in solvents used in the coating compositions, is compatible with membrane processing temperatures, sufficiently adheres to the coating during thermal processing that it does not delaminate, and dissolves readily in solvents that do not dissolve the membrane resin (such that the membrane can be released from the filament). Examples of suitable preconditioning agents include polyvinyl alcohol (PVOH), polyvinylpyrrolidone (PVP), poly(acrylic acid), and poly(methacrylic acid).

Illustratively, a PVOH stock solution can be prepared with about 5 wt % to about 15 wt % PVOH in deionized water, and cast on a filament by dipping the filament in the solution and withdrawing it to provide a coating having a thickness in the range of from about 1 to about 10 mil, and dried in an oven at a temperature in the range of from about 40° C. to about 80° C. for a period in the range of from about 1 minute to about 2 hours.

The preconditioned filament is coated with the coating composition to provide the desired coating thickness.

The coated filament is then subjected to phase inversion, which involves drying the coating containing resin(s), solvent system, and nanoparticles to remove some or all of the solvent. The coated filament can be dried, for example, by placing it in an oven at 40 to 80° C. for a period of about 1 min to about 2 hours. If desired, one or more additional coating compositions can be coated and dried in a similar manner on the filament that has been already coated and dried with the first or subsequent coating compositions

In an embodiment, the membrane-forming polymer in the first coating composition is different from the membrane-forming polymer in the second coating composition. In an embodiment, the solvent in the first coating composition is different from the solvent in the second coating composition. In an embodiment, the charged polymer present in the first coating composition is different in charge from the charged polymer present in the second coating composition. In another embodiment, the charge of the charged polymer in the first and second compositions is the same but the charged polymers are of different chemistry.

In an embodiment, the particle size of the dissolvable nanoparticles in the first coating composition is different from the particle size of the dissolvable nanoparticles in the second coating composition. Thus, the dissolvable nanoparticles in the first coating composition can be larger or smaller than the particle size of the dissolvable nanoparticles in the second coating composition.

The filament that has been coated and dried as described above is then immersed in water for a suitable period of time, for example, 1 min to about 1 hr, thereby furthering or completing the solvent removal.

The dissolvable particles are then removed from the phase inverted membrane by dissolving them in a suitable solvent. A variety of procedures are suitable for dissolving the particles. As noted above, the process should avoid using hydrofluoric acid; rather, the nanoparticles can be, and should be, dissolved using safer, more environmentally benign solvents. For example, the filament that has been coated and phase inverted can be placed in a mineral acid (e.g., HCl or H₂SO₄) at a concentration in the range of about 0.1 to about 2 moles/L for a period in the range of from about 1 minute to about 1 hour, followed by immersion in an alkaline solution (e.g., KOH or NaOH) at a concentration in the range of about 0.1 to about 4 moles/L for a period in the range of from about 30 minutes to about 24 hours, followed by washing in water (e.g., DI water) for a period in the range of about 30 minutes to about 4 hours. If desired, the resulting membrane can subsequently be dried, e.g., in an oven at a temperature in the range of from about 40° C. to about 80° C. for a period in the range of about 30 minutes to about 2 hours.

The filament is then removed from the above membrane by dissolving it in a suitable solvent. Any suitable solvent can be utilized which does not adversely affect the membrane. For example, formic acid can be used to dissolve a filament made of polycaprolactam. The resulting hollow fiber membrane is then washed with water for a suitable period of time, for example, 30 min to about 4 hr, and then dried, for example, in an oven at about 40° C. to about 80° C. for a period of about 30 min to about 2 hours.

The hollow fiber membranes have a desirable hexagonal structure in at least small regions, the structure resulting from the first set of pores in the bulk of the membrane. As illustrated in FIG. 2 (showing the first set of pores resulting from dissolving the introduced particles and the hexagonal structure representing the maximum void fraction), the maximum void fraction is 74 volume percent, and membranes according to embodiments of the invention have in the range of from about 66% to about 73% void fraction.

The surfaces of the charged hollow fiber membranes can have any suitable mean pore size, e.g., as determined by, for example, calculating the average surface pore size from an SEM at 5,000× or 20,000× magnification.

Typically, the wall thickness of the hollow fiber membranes according to embodiments of the invention is in the range of about 0.5 mil to about 6.5 mils, preferably, in the range of from about 1 mil to about 3 mils.

The membrane can have any desired critical wetting surface tension (CWST, as defined in, for example, U.S. Pat. No. 4,925,572). The CWST can be selected as is known in the art, e.g., as additionally disclosed in, for example, U.S. Pat. Nos. 5,152,905, 5,443,743, 5,472,621, and 6,074,869. Typically, the membrane has a CWST of greater than about 70 dynes/cm (about 70×10⁻⁵N/cm), more typically greater than about 73 dynes/cm (about 73×10⁻⁵N/cm), and can have a CWST of about 78 dynes/cm (about 78×10⁻⁵N/cm) or more. In some embodiments, the membrane has a CWST of about 82 dynes/cm (about 82×10⁻⁵N/cm) or more.

The surface characteristics of the charged hollow fiber membrane can be modified (e.g., to affect the CWST, to include a surface charge, e.g., a positive or negative charge, and/or to alter the polarity or hydrophilicity of the surface) by wet or dry oxidation, by coating or depositing a polymer on the surface, or by a grafting reaction. Modifications include, e.g., irradiation, a polar or charged monomer, coating and/or curing the surface with a charged polymer, and carrying out chemical modification to attach functional groups on the surface. Grafting reactions may be activated by exposure to an energy source such as gas plasma, vapor plasma, corona discharge, heat, a Van de Graff generator, ultraviolet light, electron beam, or to various other forms of radiation, or by surface etching or deposition using a plasma treatment.

A variety of fluids can be filtered in accordance with embodiments of the invention. Hollow fiber membranes according to embodiments of the invention can be used in a variety of applications, including, for example, diagnostic applications (including, for example, sample preparation and/or diagnostic lateral flow devices), ink jet applications, filtering fluids for the pharmaceutical industry, filtering fluids for medical applications (including for home and/or for patient use, e.g., intravenous applications, also including, for example, filtering biological fluids such as blood (e.g., to remove leukocytes)), filtering fluids for the electronics industry (e.g., filtering photoresist fluids in the microelectronics industry), filtering fluids for the food and beverage industry, clarification, filtering antibody- and/or protein-containing fluids, filtering nucleic acid-containing fluids, cell detection (including in situ), cell harvesting, and/or filtering cell culture fluids. Alternatively, or additionally, membranes according to embodiments of the invention can be used to filter air and/or gas and/or can be used for venting applications (e.g., allowing air and/or gas, but not liquid, to pass therethrough). Membranes according to embodiments of the inventions can be used in a variety of devices, including surgical devices and products, such as, for example, ophthalmic surgical products.

In accordance with embodiments of the invention, the charged hollow fiber membrane can be configured in a variety of configurations, e.g., the hollow fibers may be arranged in bundles, sometimes with one end blinded.

Charged hollow fiber membranes according to embodiments of the invention are typically disposed in a housing comprising at least one inlet and at least one outlet and defining at least one fluid flow path between the inlet and the outlet, wherein at least one inventive membrane or a filter including at least one inventive membrane is across the fluid flow path, to provide a filter device or filter module. In an embodiment, a filter device is provided comprising a housing comprising an inlet and a first outlet, and defining a first fluid flow path between the inlet and the first outlet; and at least one inventive hollow fiber membrane or a filter comprising at least one inventive membrane, the inventive membrane or filter comprising at least one inventive membrane being disposed in the housing across the first fluid flow path.

Preferably, for crossflow applications, at least one inventive membrane or filter comprising at least one inventive membrane is disposed in a housing comprising at least one inlet and at least two outlets and defining at least a first fluid flow path between the inlet and the first outlet, and a second fluid flow path between the inlet and the second outlet, wherein the inventive membrane or filter comprising at least one inventive membrane is across the first fluid flow path, to provide a filter device or filter module. In an illustrative embodiment, the filter device comprises a crossflow filter module, the housing comprising an inlet, a first outlet comprising a concentrate outlet, and a second outlet comprising a permeate outlet, and defining a first fluid flow path between the inlet and the first outlet, and a second fluid flow path between the inlet and the second outlet, wherein at least one inventive membrane or filter comprising at least one inventive membrane is disposed across the first fluid flow path.

The filter device or module may be sterilizable. Any housing of suitable shape and providing an inlet and one or more outlets may be employed.

The housing can be fabricated from any suitable rigid impervious material, including any impervious thermoplastic material, which is compatible with the fluid being processed. For example, the housing can be fabricated from a metal, such as stainless steel, or from a polymer, e.g., transparent or translucent polymer, such as an acrylic, polypropylene, polystyrene, or a polycarbonate resin.

The following examples further illustrate the invention but, of course, should not be construed as in any way limiting its scope.

EXAMPLE 1

This example demonstrates methods for making the conditioned substrate, resin stock solutions, and nanoparticle stock solutions.

PVOH stock solution (1): In a jacketed kettle kept at 90° C., a solution was prepared by combining 10% w/w PVOH (96% Hydrolyzed, Scientific Polymer Products) with 90% deionized water and stirring at 200 rpm for 16 h. A polycaprolactam monofilament with a diameter of 1.5 mils was dipped into PVOH stock solution (1) and placed in an oven at 80° C. for 2h.

Resin Stock Solution (1): In a jacketed kettle kept at 25° C. using a circulating bath, 20% (w/w) PES resin (BASF, Ultrason E 6020 P), 20% N-methylpyrrolidone, and 59% dimethylformamide, <1% PEG-1000, and <1% 1:1 maleic acid:methyl vinyl ether copolymer (Scientific Polymer Products) were mixed at 800 rpm using an overhead mixer for 4 h. The solution was placed under vacuum at 200 mbar for 30 minutes to deaerate the solution.

Resin Stock Solution (2): In a jacketed kettle kept at 25° C. using a circulating bath, 20% (w/w) PES resin (BASF, Ultrason E 6020 P), 20% N-methylpyrrolidone, 59% dimethylformamide, <1% PEG-1000, and <1% branched polyethylenimine (Sigma-Aldrich) were mixed at 800 rpm using an overhead mixer for 4 h. The solution was placed under vacuum at 200 mbar for 30 minutes to deaerate the solution.

Particle Stock Solution (1): In a jacketed flask kept at 25° C. using a circulating bath, a solution was prepared consisting of 1 mol/L ammonia, 8.24 mol/L ethanol, 1 mol/L methanol, 23.7 mol/L water, 0.15 mol/L tetraethoxysilane, and 0.0078 mol/L sodium metasilicate and stirred at 200 rpm for 1 h. Dynamic light scattering and SEM showed particle diameters of approximately 570 nm. The particles were centrifuged, decanted, and re-suspended in ethanol twice. They were centrifuged, decanted, and re-suspended in dimethylformamide along with 0.1% triethanolamine three times. The stock solution had a final concentration of 63% (w/w) particles.

EXAMPLE 2

This example illustrates the preparation of a charged hollow fiber membrane having a positively charged zone and a negatively charged zone.

The membrane-forming polymer was PES. Each of the two charged zones contained first set of pores of size 570 nm.

The monofilament was dipped into casting solution (1) and placed in an oven for 15 min at 60° C., followed by dipping in casting solution (2) and placing in an oven for 15 min at 60° C. The coated filament was then immersed in water at 80° C. for 1 h. The coated filament was soaked in 1 mol/L HCl for 30 min, then in 2 mol/L KOH for 18 h. The core filament was removed by soaking in formic acid for 18 h and the hollow fiber was washed with water at 25° C. for 2 h and dried at 70° C. for 30 min. SEM images of the cross-sections are shown in FIG. 3A-B. Toluidine blue stain and Ponceau S stain confirm two distinct zones, with the inner zone being negatively charged, and the outer zone being positively charged. The second set of pores in each zone was about 171 nm.

EXAMPLE 3

This example illustrates the preparation of a charged hollow fiber membrane having a negatively charged zone and a positively charged zone.

The membrane-forming polymer was PES. Each of the two charged zones contained pores of size 570 nm.

A polycaprolactam monofilament was dipped into casting solution (2) and placed in an oven for 15 min at 60° C., followed by dipping in casting solution (1) and placing in an oven for 15 min at 60° C. The coated filament was then immersed in water at 80° C. for 1 h. The coated filament was soaked in 1 mol/L HCl for 30 min, then 2 mol/L KOH for 18 h. The core filament was removed by soaking in formic acid for 18 h and the hollow fiber was washed with water at 25° C. for 2 h and dried at 70° C. for 30 min. SEM images of the cross-sections are shown in FIG. 4A-B. Toluidine blue stain and Ponceau S stain confirm two distinct zones, with the outer zone being negatively charged, and the inner zone being positively charged. The first set of pores in each zone was about 570 nm and the second set of pores in each zone was about 171 nm.

All references, including publications, patent applications, and patents, cited herein are hereby incorporated by reference to the same extent as if each reference were individually and specifically indicated to be incorporated by reference and were set forth in its entirety herein.

The use of the terms “a” and “an” and “the” and “at least one” and similar referents in the context of describing the invention (especially in the context of the following claims) are to be construed to cover both the singular and the plural, unless otherwise indicated herein or clearly contradicted by context. The use of the term “at least one” followed by a list of one or more items (for example, “at least one of A and B”) is to be construed to mean one item selected from the listed items (A or B) or any combination of two or more of the listed items (A and B), unless otherwise indicated herein or clearly contradicted by context. The terms “comprising,” “having,” “including,” and “containing” are to be construed as open-ended terms (i.e., meaning “including, but not limited to,”) unless otherwise noted. Recitation of ranges of values herein are merely intended to serve as a shorthand method of referring individually to each separate value falling within the range, unless otherwise indicated herein, and each separate value is incorporated into the specification as if it were individually recited herein. All methods described herein can be performed in any suitable order unless otherwise indicated herein or otherwise clearly contradicted by context. The use of any and all examples, or exemplary language (e.g., “such as”) provided herein, is intended merely to better illuminate the invention and does not pose a limitation on the scope of the invention unless otherwise claimed. No language in the specification should be construed as indicating any non-claimed element as essential to the practice of the invention.

Preferred embodiments of this invention are described herein, including the best mode known to the inventors for carrying out the invention. Variations of those preferred embodiments may become apparent to those of ordinary skill in the art upon reading the foregoing description. The inventors expect skilled artisans to employ such variations as appropriate, and the inventors intend for the invention to be practiced otherwise than as specifically described herein. Accordingly, this invention includes all modifications and equivalents of the subject matter recited in the claims appended hereto as permitted by applicable law. Moreover, any combination of the above-described elements in all possible variations thereof is encompassed by the invention unless otherwise indicated herein or otherwise clearly contradicted by context. 

1. A charged hollow fiber membrane comprising: (i) an inner surface; (ii) an outer surface; (iii) a porous bulk disposed between the inner surface and the outer surface, wherein the porous bulk comprises at least a first region including: a) a first set of pores having a controlled pore size and having outer rims; b) a second set of pores connecting the outer rims of the first set of pores, wherein the pore size of the first set of pores is greater than the pore size of the second set of pores; and c) a polymer matrix supporting the first set of pores; and (iv) at least one charged zone disposed on the inner surface, on the outer surface, and/or in the porous bulk.
 2. The charged hollow fiber membrane of claim 1, which includes at least two charged zones.
 3. The charged hollow fiber membrane of claim 1, wherein at least one charged zone is negatively charged and is disposed in the porous bulk close to the inner surface and at least one other charged zone is positively charged and is disposed in the porous bulk close to the outer surface.
 4. The charged hollow fiber membrane of claim 1, wherein at least one charged zone is positively charged and is disposed in the porous bulk close to the inner surface and at least one other charged zone is negatively charged and is disposed in the porous bulk close to the outer surface.
 5. The charged hollow fiber membrane of claim 3, which includes a neutral zone between the negatively charged zone and the positively charged zone.
 6. The charged hollow fiber membrane of claim 2, wherein the negatively charged zone comprises a negatively charged polymer.
 6. The charged hollow fiber membrane of claim 1, wherein the positively charged zone comprises a positively charged polymer.
 7. The charged hollow fiber membrane of claim 1, wherein the pore size of the first set of pores is in the range of from about 50 nm to about 1000 nm.
 8. The charged hollow fiber membrane of claim 1, wherein the pore size of the second set of pores is in a ratio in the range of about 0.2 to about 0.4 times the pore size of the first set of pores.
 9. The charged hollow fiber membrane of claim 1, wherein the porous bulk further comprises at least a second region including: d) a third set of pores having a controlled pore size and having outer rims; e) a fourth set of pores connecting the outer rims of the third set of pores, wherein the pore size of the third set of pores is greater than the pore size of the fourth set of pores; and (f) a polymer matrix supporting the third set of pores.
 10. The charged hollow fiber membrane of claim 9, wherein the pore size of the fourth set of pores is in a ratio in the range of about 0.2 to about 0.4 times the pore size of the third set of pores.
 11. The charged hollow fiber membrane of claim 9, wherein the pore size of the third set of pores is at least 10% different from the pore size of the first set of pores.
 12. A method of making a charged hollow fiber membrane, the method comprising: (a) forming at least one coating composition comprising a solvent, dissolvable silica nanoparticles, a membrane-forming polymer, and a charged polymer; (b) coating the at least one coating composition onto a filament; (c) carrying out phase inversion of the at least one coating composition, or the coating compositions, coated onto the filament; (d) dissolving the dissolvable silica nanoparticles and removing the filament from the coated filament to obtain a charged hollow fiber membrane; and optionally (e) washing the charged hollow fiber membrane obtained in (d).
 13. The method of claim 12, which includes: forming a first coating composition and a second coating composition, each comprising a solvent, a set of dissolvable silica nanoparticles, a membrane-forming polymer, and a charged polymer in (a), and coating the coating the first and the second coating compositions onto the filament in (b).
 14. The method of claim 13, wherein the particle size of the dissolvable silica nanoparticles in the first coating composition is different from the particle size of the dissolvable silica nanoparticles in the second coating composition.
 15. The method of claim 13, wherein the membrane-forming polymer in the first coating composition is different from the membrane-forming polymer in the second coating composition.
 16. The method of claim 12, wherein the solvent in the first coating composition is different from the solvent in the second coating composition.
 17. The method of claim 12, wherein the filament is a polymer filament.
 18. (canceled)
 19. The method of claim 12, wherein the at least one coating composition is coated by dip coating.
 20. (canceled)
 21. The method of claim 1, wherein the dissolvable silica nanoparticles are dissolved by contacting the filament after (c) with an acid and an alkali.
 22. (canceled)
 23. A method of filtering a fluid, the method comprising passing the fluid through the charged hollow fiber membrane of claim
 1. 